Laird Technologies Web site: Item # Tmate 2910, Tmate 2900 Series Phase Change Material Tmate 2900 Series Phase Change Material SPECIFICATIONS Tmate 2900 is a reusable phase change material designed for ease of testing and rework ability. Tmate 2900 has a composite construction of a special malleable metal alloy and a high performance phase change material. At 50ºC, Tmate 2900 begins to soften and flow, filling the microscopic irregularities of the thermal solution, thus reducing thermal resistance. Tmate 2900 shows no thermal performance degradation after 1000 hours at 130ºC, or after 500 cycles, from -25ºC to 125ºC. The phase change material softens and does not fully change state resulting in minimal migration pump out at operating temperatures. Tmate 2900 is available in three thicknesses, in. mm , in. mm and in. mm . Construction and Composition Color Test Method - Color Thickness Tolerance Density Shelf Life Temperature Range Phase Change Softening Range "Burn In" Temperature Thermal Resistance at 20 psi Test Method - Thermal Resistance Volume Resistivity Test Method - Volume Resistivity Foil coated on one side with phase change material Silver Yellow Visual inches mm inches mm g/cc 1 year -25 to 125 ºC 50 to 70 ºC 70ºC for 5 minutes 10.1.16800ºCºC-c-imn22//WW ASTM D5470 modified 5 x 1012 ohm-cm ASTM D257 4/22/2011 \| Page 1 of 2 Dielectric Constant at 1 MHz Test Method - Dielectric Constant Sheet Size ASTM D150 9 x 9 inches 4/22/2011 \| Page 2 of 2

PDF Datasheet Preview

Laird Technologies Web site:

Item # Tmate 2910, Tmate 2900 Series Phase Change Material

Tmate 2900 Series Phase Change Material

SPECIFICATIONS

Tmate 2900 is a reusable phase change material designed for ease of testing and rework ability. Tmate 2900 has a composite construction of a special malleable metal alloy and a high performance phase change material. At 50ºC, Tmate 2900 begins to soften and flow, filling the microscopic irregularities of the thermal solution, thus reducing thermal resistance. Tmate 2900 shows no thermal performance degradation after 1000 hours at 130ºC, or after 500 cycles, from -25ºC to 125ºC. The phase change material softens and does not fully change state resulting in minimal migration pump out at operating temperatures. Tmate 2900 is available in three thicknesses, in. mm , in. mm and in. mm .

Construction and Composition Color Test Method - Color Thickness Tolerance Density Shelf Life Temperature Range Phase Change Softening Range "Burn In" Temperature Thermal Resistance at 20 psi Test Method - Thermal Resistance Volume Resistivity Test Method - Volume Resistivity

Foil coated on one side with phase change material Silver Yellow Visual
inches mm inches mm g/cc
1 year -25 to 125 ºC 50 to 70 ºC 70ºC for 5 minutes 10.1.16800ºCºC-c-imn22//WW ASTM D5470 modified 5 x 1012 ohm-cm ASTM D257
4/22/2011 | Page 1 of 2

Dielectric Constant at 1 MHz Test Method - Dielectric Constant Sheet Size

ASTM D150 9 x 9 inches
4/22/2011 | Page 2 of 2