3.0mm PVA Water-Soluble Filament 1kg SKU FIT0360 INTRODUCTION Polyvinyl alcohol PVOH, PVA, or PVAl is a water-soluble synthetic polymer. It has the idealized formula [CH2CH OH ]n. It is widely used in papermaking, textiles, and a variety of coatings. Colourless and odorless, PVA is sometimes supplied as beads or as solutions in water. In 3D Printing, PVA is a wonderful support material since it is water soluble. It will disolve faster in a heated agitated bath, and it's ideally biodegradable! How To Use This material absorbs moisture once the packaging is opened and should therefore be processed only from the unopened original bag. Otherwise bubbles may occur in the molding. Damp material can be dried at 60 80C for hours in a circulated air dryer. Suitable processing temperature should not exceed 160-175C because at higher temperatures the material suffers thermal damage. Residence time should be as short as possible, minutes at most. Dissolving PVA dissolves rapidly with simple submersion. A 10cm cube printed with no one surface at 20% infill and submerged in one cup of room-temperature water will begin to break apart within 20 minutes, and entirely within 24 hours. To speed up the dissolution, gentle stirring can be applied. Warm water may also enhance the process. The water will quickly become an opaque white, and take on the appearance and consistency of wood glue. SPECIFICATION • Color pale yellow • Spool Size 170X170X55mm • Spool hub hole 50mm 1.97" • Diameters 3.00mm 0.12" ±0.05 mm 0.0019" • Net Weight kg lbs • Melting temperature 160°C • Nozzle temperature 210-215°C • Density 1.3g/cm3 SHIPPING LIST • 3.0mm PVA 1kg x1 Powered By DFRobot 2008-2016

PDF Datasheet Preview

3.0mm PVA Water-Soluble Filament 1kg

SKU FIT0360

INTRODUCTION

Polyvinyl alcohol PVOH, PVA, or PVAl is a water-soluble synthetic polymer. It has the idealized formula [CH2CH OH ]n. It is widely used in papermaking, textiles, and a variety of coatings. Colourless and odorless, PVA is sometimes supplied as beads or as solutions in water. In 3D Printing, PVA is a wonderful support material since it is water soluble. It will disolve faster in a heated agitated bath, and it's ideally biodegradable!

How To Use This material absorbs moisture once the packaging is opened and should therefore be processed only from the unopened original bag. Otherwise bubbles may occur in the molding. Damp material can be dried at 60 80C for hours in a circulated air dryer. Suitable processing temperature should not exceed 160-175C because at higher temperatures the material suffers thermal damage. Residence time should be as short as possible, minutes at most.

Dissolving PVA dissolves rapidly with simple submersion. A 10cm cube printed with no one surface at 20% infill and submerged in one cup of room-temperature water will begin to break apart within 20 minutes, and entirely within 24 hours. To speed up the dissolution, gentle stirring can be applied. Warm water may also enhance the process. The water will quickly become an opaque white, and take on the appearance and consistency of wood glue.

SPECIFICATION
• Color pale yellow
• Spool Size 170X170X55mm
• Spool hub hole 50mm 1.97"
• Diameters 3.00mm 0.12" ±0.05 mm 0.0019"
• Net Weight kg lbs
• Melting temperature 160°C
• Nozzle temperature 210-215°C
• Density 1.3g/cm3